Insert for a wind turbine blade root

ABSTRACT

An insert (105) for a wind turbine blade root. The insert (105) has a bushing (40) and an outer surface with circumferential annular grooves (68). A transition layer 5 (102) is built up around the bushing (40). The transition layer (102) has fibrous material sheet layers and filamentary material windings (80) in the grooves which alternate with fibrous plies (98) covering the grooves (68). Each fibrous ply (98) is anchored into the grooves (68) by the windings (80). Fibrous battens (148) are fitted around the transition layer (102) to form an insert body (108). Each batten (148) 10 has a deltoid cross-section so that the battens give the insert a quadrilateral or trapezoidal cross-section.

FIELD OF THE INVENTION

The present invention relates to an insert for a wind turbine blade root, and a method of manufacturing such an insert.

BACKGROUND OF THE INVENTION

WO2010/041008 discloses an insert for forming an end connection for a uni-axial composite material, for example, of a wind turbine hub. The insert comprises a sleeve having a plurality of fibres with a multi-axial arrangement. At least a portion of the interior surface of the sleeve comprises a thread formation. The thread may be cut into the sleeve, or the sleeve may be formed over a mandrel. A helical thread insert may be used to provide an insert that is readily reusable.

A wind turbine blade for a large horizontal axis wind turbine may have significant mass, perhaps in the region of 10 tonnes or more, up to 30 tonnes or more. Blades are fastened to a hub to make up a rotor. A rotor rotates on a main shaft to drive a generator. Blades are attached at their root end to a hub flange. A blade is typically connected to a hub flange using a group of bolts. The stresses on a blade hub connection are considerable, owing chiefly to blade mass and wind force, as well as the effect of perpetual rotation of the rotor, which tends to vary the degree and direction of the forces on the blade with every rotation of the rotor. Vibrations in the system can also be considerable. With an expected lifetime of 20 years and more, the fatigue performance of the blade hub connection is critical. A bolt group, often known as stud bolts, may be connected to the blade root using threaded bushings, embedded into the root end of a blade. Such bushings are usually cylindrical, often made of steel. The bushings transfer the loads from the blade to the stud bolts. The stud bolts transfer those loads to the hub, which is a rigid, often cast, component. Considering the fatigue requirements placed on a blade hub connection, the manner of embedding bushings into a blade root can be critical. The present invention addresses the design of an insert, into which a bushing is embedded, and methods of preparing the same. The insert, containing a bushing, may be embedded in a blade root along with other inserts. The blade root, with its inserts, thereby presents a connection face for a bolted connection to a hub.

SUMMARY OF THE INVENTION

A first aspect of the invention provides an insert for a wind turbine blade root, the insert comprising: an insert body; a bushing with a threaded bore and an outer surface with circumferential grooves; and a transition layer comprising fibrous plies covering the bushing outer surface, and windings over said fibrous plies such that successive said plies alternate with said windings, wherein each fibrous ply is anchored into the grooves by an associated set of the windings, and said insert body surrounds said transition layer.

The transition layer provides a fatigue-resistant interface layer between the bushing and the insert body.

Preferably the insert further comprises an extension portion extending away from the bushing to a tip, wherein the extension portion tapers as it extends away from the bushing to the tip.

Preferably the bushing is an elongate bushing extending along a main axis. Successive plies in said transition layer preferably alternate with said windings in a radial direction about said bushing. The bushing comprises an internal bore. The bore preferably comprises a threaded portion in the form of an internal thread. In embodiments, the bushing may comprise an end region and a body region. The end region may contain the threaded bore. The outer surface of the body region may comprise the circumferential grooves. In embodiments, the bushing end region may be offset from the body region so that none of the grooves encircle the internal thread. Alternatively, the grooves may be distributed along a full length of the bushing so that some of the grooves encircle the internal thread.

Optionally the end region of the bushing has a minimum wall thickness at the threaded bore which is greater than a maximum wall thickness of the body region, in particular at the circumferential grooves about said body region. The minimum wall thickness at the threaded bore may coincide with grooves of an internal thread in the threaded bore. The internally threaded region of a bushing is an area of high load transfer between a tension bolt in the bushing and the insert body. The high minimum wall thickness at the threaded bore makes the bushing's end region more crack-resistant.

Optionally the end region of the bushing has a cylindrical outer surface.

The outer surface of the bushing typically has a sectional profile across the grooves with a series of crests and troughs. Each crest may be pointed, but more preferably each crest is flat, or rounded. Where the crests are rounded, then typically they are each rounded with a radius of curvature greater than 1 mm, greater than 2 mm, or greater than 3 mm. Each trough may be pointed, but more preferably each trough is flat, or rounded. Where the troughs are rounded, then typically they are each rounded with a radius of curvature greater than 1 mm, greater than 2 mm, or greater than 3 mm.

The sectional profile may be a square-wave or triangular-wave profile, but more typically the crests and/or the troughs are rounded. Most preferably the sectional profile is a sinuous profile with a series of rounded crests and rounded troughs.

Preferably each fibrous ply, when wrapped and bound around the undulating bushing surface, exhibits corrugations, resulting from being anchored into the grooves by the windings. The corrugations exhibit undulations which may reduce in amplitude from ply-to-ply in a direction away from the bushing outer surface. More specifically, the corrugations may be said to reduce in amplitude progressively, from ply-to-ply, in a radial direction away from the bushing. Optionally the corrugations' amplitude may reduce to zero so the transition layer may effectively have one or more additional fibrous plies which are un-corrugated. Herein, the term “from ply-to-ply” may refer to a progression from one ply to a subsequent ply, e.g. in a direction radially away from the bushing. In embodiments, the corrugations may reduce in height progressively, from each ply to each subsequent ply, in a radial direction away from the bushing.

Each fibrous ply is anchored into the grooves by an associated set of the windings. Each set of the windings may have only a single winding per groove, or one or more of the sets of the windings may have multiple windings per groove. The number of windings per groove applied over a given fibrous ply may be constant from ply-to-ply, or it may vary—for instance by increasing in a radial direction away from the bushing. Optionally one or more of the sets of said windings have a number of windings per groove greater than a number of windings per groove of a set of said windings anchoring a lower fibrous layer. By way of example, a first fibrous ply may be anchored into the grooves by an associated first set of windings with two windings per groove, and a second fibrous ply may be anchored into the grooves by an associated second set of windings with four windings per groove. The number of windings per groove may vary from set-to-set, or there may be only a single increase—for instance there may be two inner sets of windings with two windings per groove, and two outer sets of windings with four windings per groove.

Preferably a winding may comprise a bundle of filaments. Preferably each winding may comprise a bundle of filaments. The number of filaments per groove may be constant from set-to-set, or it may vary—for instance increasing in a radial direction away from the bushing. This may be achieved by changing the number of filaments per winding, or by changing the number of windings per groove.

Preferably the windings are tows of filamentary material, for instance carbon filamentary material.

The circumferential grooves may be connected end-to-end so they that collectively form a single continuous helical thread (each circumferential groove being a respective turn of the thread). More preferably, the circumferential grooves are multiple, circumferential annular grooves—in other words they are not helical, but instead are unconnected. Typically, the circumferential annular grooves alternate with circumferential annular ridges. The windings in adjacent annular grooves may be unconnected, but more typically the windings are formed by a filamentary material with connecting sections of the filamentary material which ride over the circumferential annular ridges between the circumferential annular grooves and connect together windings in adjacent circumferential annular grooves. An annular groove shape enables multiple windings to be wrapped into each groove with a single pass of a spool of the filamentary material.

The grooves may have a depth A and may be separated by a pitch P. Preferably the grooves are relatively shallow and the pitch is relatively large, so the ratio A/P is low. This makes the walls of the groove less steep and hence easy to anchor the fibrous plies into the grooves. Typically, A/P is less than 1, less than ⅔, less than ½, or less than ¼. Preferably A/P is greater than 1/10.

Typically, the grooves are separated by a pitch which is greater than 6 mm, greater than 7 mm, or greater than 8 mm.

Typically, the grooves have a depth which is less than 4 mm, less than 3 mm, or less than 2 mm.

The insert body may be made of fibrous material, for example fibre-reinforced composite material.

The windings and fibrous plies which make up the transition layer may preferably be applied “dry” around the bushing, i.e. without uncured resin. These may then be infused with a matrix material which serves to bond the transition layer to the bushing.

Preferably, the infusion step may take place in a resin transfer moulding (RTM) process with additional, preferably fibrous, material positioned around the transition layer to form the insert body. In this way, the transition layer and the surrounding material of the insert body are infused together with a matrix material. The transition layer is thereby fixed in the resulting insert body. The transition layer thereby serves to firmly anchor the bushing within the insert body.

Typically, each fibrous ply of the transition layer is formed from one or more layers of fibrous sheet material. In some embodiments, each fibrous ply comprises a single layer of fibrous sheet material. In other embodiments, one or more the fibrous plies may be formed from multiple layers of fibrous sheet material so as to constitute a multi-layer ply. Each multi-layer ply may be formed by wrapping two or more turns of the fibrous sheet material onto the bushing one after the other to form a spiral. Alternatively, each multi-layer ply may be formed by simultaneously wrapping two or more layers of the fibrous sheet material onto the bushing in a single turn.

The fibrous plies are anchored into the circumferential grooves by the windings. Each layer of the fibrous sheet material which forms a fibrous ply may exhibit a fibre direction in a single direction, e.g. in the case of uni-axial fabric. Alternatively, the fibrous sheet material may exhibit more than one fibre direction, such as in the case of bi-axial, tri-axial or multi-axial fibrous sheet material, or fabric. In embodiments, fibrous sheet material may be wrapped around a bushing such that the fibre direction of a resulting fibrous ply may run across the grooves at 90° to the grooves, or at an oblique angle to the grooves such as 45°.

The insert body may comprise two or more fibrous battens fitted around the transition layer. Each batten may have a deltoid cross-section so that together, a set of e.g. four battens may give the insert a quadrilateral cross-sectional shape. The insert body may in particular have a rectangular or trapezoidal cross-section. The term “rectangular” is used herein to denote a quadrilateral shape with right-angled corners, which may be square or non-square. The corners may be sharp or rounded. Optionally the insert body further comprises a fibrous outer shell wrapped around the fibrous battens.

Typically, each fibrous batten may have a concave inner face. This concave inner face may contact the transition layer. Each fibrous batter may also have a pair of outer faces which meet at a corner, and which may be sharp or rounded.

The first aspect of the invention also provides a method of manufacturing an insert for a wind turbine blade root, the method comprising: providing a bushing, wherein the bushing has a threaded bore and an outer surface with circumferential grooves; wrapping a first fibrous ply around the bushing so that it overlies the grooves; winding filamentary material around the first fibrous ply to form a first set of windings which draw the fibrous ply into the grooves so that the first fibrous ply is anchored into the grooves by the first set of windings; said first set of windings and said first fibrous ply forming a transition layer around the bushing; positioning material around the transition layer to form an insert body; placing the bushing, the transition layer and the insert body in an infusion mould; injecting a matrix material into the infusion mould so that the matrix material infuses the transition layer; and curing the matrix material. The first fibrous ply deforms during the process to adopt a corrugated profile, with corrugations anchored into the grooves. The method results in an insert comprised of an insert body in which a bushing is embedded.

The transition layer may consist of only a single fibrous ply and a single set of windings, but more typically the method further comprises: wrapping a second fibrous ply around the bushing so that it overlies the grooves; winding filamentary material around the second fibrous ply to form a second set of windings which draw the second fibrous ply into the grooves so that the second fibrous ply is anchored into the grooves by the second set of windings; wherein the first and second sets of windings and the first and second fibrous plies form the transition layer, and the first and second sets of windings alternate with the first and second fibrous plies.

Optionally the first and/or second set of windings has multiple windings per groove.

Optionally the first and second sets of windings are formed by rotating the bushing, each rotation of the bushing forming a single winding, and the second set of windings has more windings per groove than the first set of windings.

Further fibrous plies may be wrapped around the bushing, so the transition layer has three, four or more fibrous plies alternating with associated sets of windings.

The insert body may be positioned around the transition layer by wrapping or otherwise forming the material around the transition layer. Optionally the insert body is positioned by fitting two or more fibrous battens around the transition layer, wherein each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section, such as a rectangular or trapezoidal cross-section, and the matrix material infuses the transition layer and optionally also the fibrous battens.

The matrix material injected into the infusion mould may infuse the insert body, or the insert body may be pre-impregnated or pre-cured before it is placed in the infusion mould so the matrix material injected into the infusion mould does not infuse into the insert body. In this case the matrix material injected into the infusion mould only infuses the transition layer and any other porous parts of the insert.

The assembly placed in the infusion mould may be used to form only a single insert, or an intermediate product may be placed in the infusion mould and then cut in half after it is removed from the mould to produce two matching inserts.

A further aspect of the invention provides an insert for a wind turbine blade root, the insert comprising a bushing embedded in an insert body; said bushing having a threaded bore; and wherein said insert body comprises two or more fibrous battens fitted around the bushing, wherein each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section, such as a rectangular or trapezoidal cross-section.

In a preferred embodiment the insert body has four fibrous battens each with a deltoid cross-section; and in other embodiments the insert body has two battens, each batten having a pair of lobes and each lobe having a deltoid cross-section.

Optionally the insert body further comprises a fibrous outer shell wrapped around the fibrous battens.

By way of example, each batten may comprise a pultruded preform; or an assembly of ropes, rods or other elongate members.

The insert may further comprise a fibrous transition layer extending between the bushing and the insert body. Preferably, the fibrous transition layer may extend between the bushing and the battens. This transition layer may have a generally sleeve-like shape. The transition layer may exhibit a generally cylindrical interface with the bushing. Preferably, the transition layer may be anchored into circumferential grooves on a bushing outer surface, as discussed in connection with the first aspect of the invention. Preferably the transition layer may comprise sheets of fibrous material wrapped around the bushing by windings of filamentary material. Preferably, the windings of filamentary material are applied tightly, in a manner to anchor layers of fibrous material in the bushing's surface grooves. The transition layer thereby provides an excellent fatigue-resistant interface layer between the bushing and the insert body.

The insert extends in a lengthwise direction along a main axis, and the fibrous battens typically comprise fibres extending substantially in the lengthwise direction (for instance +/−5°). Typically, the fibres of the battens are uniaxial. The battens may be of pultruded fibrous composite material. The fibres in the battens may be pultruded with a more or less viscous liquid resin matrix material and subsequently cured. The cured, pultruded battens may be moulded together with wrapped bushings to make up inserts. This may be carried out in an RTM process in which resin may be infused around the battens and into the transition layer. After curing, the battens are thereby co-bonded within the insert body. The transition layer is firmly integrated into the insert body and firmly fixed around the bushing.

Alternatively, the battens may be pultruded using a dry binder material such as powder particles of a binder material. For example, continuous filaments of e.g. glassfibre or carbon fibre may be passed through a pultrusion die together with a proportion of powder binder material. The binder material may for example be a thermoplastic resin or any resin capable of melting and re-solidifying to locally bind neighbouring filaments together. In embodiments, the pultrusion die may be heated. The heated die may be heated enough to cause the binder particles in the pultrudate to melt as they pass through the die. This melting of powder particles locally causes the particle material to flow around neighbouring filaments, e.g. by capillary action, as the filaments are compacted together at the pultrusion die. Upon cooling, the binder material locally binds pultruded filaments together. The pultruded batten may thereby have shape integrity, while remaining porous to liquids. The binder material may preferably make up 10% or less by volume of the finished pultruded batten. The binder material may preferably make up 7% or less by volume of the finished pultruded batten. The binder material may preferably make up 5% or less by volume of the finished pultruded batten. By including a lower binder material proportion, the porosity of the pultruded batten can be increased. A higher porosity of the pultruded batten may enhance the structural integrity of the insert body by allowing penetration by an infusion resin into the pultruded batten. If one or more pultruded battens are integrated into the insert during the RTM process, then the battens, the transition layer, and any other parts of the insert body may be co-cured after infusion. Co-curing the elements which make up the insert body can increase the structural integrity of the insert body.

In any case, the transition layer may preferably be co-cured with the insert body, thereby enhancing the bond between the transition layer and the insert body.

Typically, each fibrous batten has a concave inner face, and a pair of outer faces which meet at a corner which may be sharp or rounded.

This aspect of the invention also provides a method of manufacturing an insert for a wind turbine blade root, the method comprising: providing a bushing, wherein the bushing has a threaded bore; fitting two or more fibrous battens around the bushing, wherein each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section, such as a rectangular or trapezoidal cross-section; placing the bushing and the battens in an infusion mould; injecting a matrix material into the infusion mould so that the matrix material infuses the insert; and curing the matrix material to thereby form an insert body with an embedded bushing.

Optionally the method further comprises generating a fibrous transition layer around the bushing. The fibrous battens may be fitted around the transition layer; and matrix material may be infused into the transition layer and around or into the battens. Such a transition layer provides a secure interface between the bushing and the insert body.

Optionally the method further comprises wrapping a fibrous outer shell around the outside of the fibrous battens. Preferably, the fibrous outer shell may define the periphery of the insert body. Preferably, the fibrous outer shell may be dry fibrous material sheets. During infusion of the insert, the matrix material also infuses the fibrous outer shell. Such a fibrous outer shell has the advantage of securely fixing the battens in place. The fibrous outer shell may additionally serve to conform the fibrous material of the insert body to the shape of the RTM mould, prior to resin-infusion thereof.

The matrix material injected into the infusion mould may infuse the battens, or the battens may be pre-impregnated or pre-cured before they are placed in the infusion mould so the matrix material injected into the infusion mould does not infuse into the battens. In this case the matrix material injected into the infusion mould only infuses through the transition layer, the outer shell and other porous parts of the insert.

The infusion mould typically comprises a mould cavity containing the insert, and at least part of the mould cavity has a quadrilateral cross-section, such as a rectangular or trapezoidal cross-section. Optionally the infusion mould has two mould parts which meet at a split line and can be separated to remove the insert. Preferably the split line coincides with a diagonal of the quadrilateral cross-section.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the invention will now be described with reference to the accompanying drawings, in which:

FIG. 1 shows a wind turbine;

FIG. 2 shows a blade of the wind turbine of FIG. 1;

FIG. 3 shows a root end of the blade of FIG. 2;

FIG. 4 is an enlarged end view of part of the root end of FIG. 3;

FIG. 5 shows a wind turbine blade root insert;

FIG. 6a is a cross-sectional view along the length of a double-ended blank which is cut in half to form a matching pair of inserts;

FIG. 6b is a cross-sectional view through the assembly shown in FIG. 6, sectioned along a line y-y and additionally showing lay-up elements around the transition layer;

FIG. 6c shows a sectional profile across the grooves of a bushing with a series of shallow and sinuous crests and troughs;

FIG. 7 is a schematic side view of a bushing wrapped in a transition layer and showing connecting sections of filamentary material between adjacent grooves;

FIG. 8 is a sectional side view showing two grooves and the transition layer covering the grooves;

FIG. 9 is a sectional side view showing two grooves and an alternative transition layer covering the grooves;

FIG. 10 is a sectional side view showing two grooves and a further alternative transition layer covering the grooves;

FIG. 11a shows a filamentary material being wound onto a spindle to form a set of windings over a material wrapping layer;

FIG. 11b shows fibrous sheet material being wrapped around the spindle;

FIG. 12 shows filamentary material being wound around battens to secure its elements in place;

FIG. 13 is a figurative, isometric view showing pultruded battens fitted around one of the bushings;

FIG. 14 shows an alternative arrangement in which the battens are formed from glass rods;

FIG. 15 shows an alternative batten formed from glass rods of varying cross section;

FIG. 16 shows an infusion moulding arrangement;

FIG. 17 is an isometric view of a blank;

FIG. 18 is a side view of the blank of FIG. 17;

FIG. 19 is a plan view of the blank of FIG. 17;

FIG. 20 is a bottom view of the blank of FIG. 17;

FIG. 21 is a cross-sectional view of the second end portion of the blank of FIG. 17;

FIG. 22 is a cross-sectional view half way along the blank of FIG. 17;

FIG. 23 is a cross-sectional view of the first end portion of the blank of FIG. 17;

FIG. 24 is a plan view of an insert cut from the blank of FIG. 17;

FIG. 25 is a bottom view of the insert of FIG. 24;

FIG. 26 is a side view of the insert of FIG. 24;

FIG. 27 shows a diagonal split infusion mould arrangement;

FIG. 28 shows a cross-section through a first, lobed batten arrangement;

FIG. 29 shows a cross-section through a second, lobed batten arrangement;

FIG. 30 shows a diagonal cross-sectional view of one end of a blank showing an embedded bushing;

FIG. 31 is an isometric view of an end cap;

FIG. 32 shows a blank;

FIG. 33 shows an isometric view showing the outer profile of a blank with an alternative geometry.

DETAILED DESCRIPTION OF EMBODIMENTS

FIG. 1 shows a horizontal axis wind turbine 10. The wind turbine 10 comprises a tower 12 supporting a nacelle 14 to which a rotor 16 is mounted. The rotor 16 comprises a plurality of wind turbine blades 18 that extend radially from a central hub 19. In this example, the rotor 16 comprises three blades 18.

FIG. 2 is a view of one of the blades 18. The blade 18 extends from a generally circular root 20 to a tip 22 in a longitudinal ‘spanwise’ direction, and between a leading edge 24 and a trailing edge 26 in a transverse ‘chordwise’ direction. The blade 18 comprises a shell 27 which may be formed primarily of fibre-reinforced plastic (FRP). The blade 18 comprises a suction surface 28 and a pressure surface 29. The suction and pressure surfaces define a thickness dimension of the blade.

The blade 18 transitions from a circular profile to an airfoil profile moving from the root 20 of the blade 18 towards a shoulder 25 of the blade 18, which is the widest part of the blade 18 where the blade has its maximum chord. The blade 18 has an airfoil profile of progressively decreasing thickness in an outboard portion of the blade 18, which extends from the shoulder 25 to the tip 22 of the blade 18.

FIG. 3 shows the root 20 of one of the blades 18, and FIG. 4 is an end view of a sector of the root 20. The root 20 is preferably attached to the hub 19 by stud-bolts (not shown) which may extend from or through a hub flange (not shown) into metal bushings 40, four of which are shown in FIG. 4. Each bushing extends in a longitudinal direction and has an internal axial bore 109. Each steel bushing 40 may be embedded in an insert 105 shown in FIG. 5. The insert 105 has an insert body 108 in which the bushing 40 is embedded. The inserts 105 may have a quadrilateral, preferably trapezoidal, cross section and may be laid side by side in a ring around the circumference of the root 20. The inserts 105 may be embedded between walls 41 and 42. These walls 41 and 42 may in particular be of glass fibre reinforced composite material. In the illustrated embodiment, composite wall 41 forms an outside layer of the shell 27 at the blade root 20 while composite wall 42 forms an inside layer of the shell 27 at the root 20. The inserts 105 may be placed in a mould and then integrated with the blade shell 27 through a resin infusion moulding process such as vacuum infusion. To achieve this, the inserts 105 may be pre-manufactured and laid into the mould by positioning them on lay-up material for the shell 27. Additional lay-up material may be applied over the inserts 105 in the mould, prior to infusion.

Note that in embodiments, the side faces 143 of the inserts 105 are preferably planar so that the inserts 105 can be arranged, as shown in FIG. 4, in a continuous ring with the planar side faces 143 of adjacent inserts 105 in abutting contact with each other. If the inserts 105 have a slightly trapezoidal shape, then the respective side faces 143 may be arranged side-by-side to form a circular arrangement as illustrated in FIGS. 3 and 4, without requiring wedge-shaped spacers between them.

Aspects of a preferred method of manufacturing a matching pair of the inserts 105 are shown in FIGS. 6a -16. First, a double-ended spindle 167 may be set up, onto which a transition layer 102 may be made up. Advantageously, two bushings 40 may be longitudinally spaced at either end of a longitudinal core 62 to form the spindle 167. The illustrated spindle 167 comprises a core 62 with frustoconical ends 63, and a pair of steel bushings 40 which each have frustoconical recesses 65 into which the ends 63 of the core may be push-fitted as shown in FIG. 6a . The core 62 may be made from a variety of materials, such as polyethylene terephthalate (PET) foam, pultruded glass, glass-fibre reinforced composite material, or wood.

With reference to FIG. 30, a bushing 40 may serve both to transfer loads between a hub connection element, such as a stud bolt (not shown), and the bushing 40, as well as to transfer loads between the bushing 40 and the insert body 108, the insert 105 being embedded in a wind turbine blade root 20. For transferring loads between a hub connection element and the bushing 40, the bushing may be provided with an internal bore 109, the internal bore 109 in turn having an engagement element 66 for engagement with a hub connection element (not shown). In the case illustrated, the bushing 40 may have an internal thread 66 for engagement with a stud bolt (not shown), for connection to a wind turbine hub. In addition, the bushing 40 may have a textured external surface (see grooves 68) for improving load transfer between the bushing 40 and the insert body 108. In FIG. 30, the textured outer surface 68 of the bushing 40 extends axially adjacent the engagement element 66. This may serve to maximise the area available on the bushing 40 surface for load transfer to the insert body 108. In other words, the two load transfer arrangements at the bushing 40 may be axially coincident. In order to improve the performance of a bushing 40, it may be desirable to axially separate those areas which perform the respective load transfer functions. Such an axial separation may reduce local peak loads in the bushing 40 and is illustrated by way of example in FIG. 6a . Accordingly, a bushing 40 may include an end region 61 which terminates in a planar end face 61 a at a root end of the bushing, and a body region 59 which extends from the end region 61 to the opposite end of the bushing. The end region 61 may be non-textured, i.e. it may have a predominantly smooth outer surface. By smooth is meant predominantly cylindrical, and preferably without external surface features. A smooth surface may be roughened for better adhesion to resin, although such roughening may not be regarded as a surface feature in this context. A body region 59 may be provided with a textured outer surface for engagement between the bushing 40 and the insert body 108. In such an arrangement, with the textured outer surface of the body portion 59 axially offset from the smooth, cylindrical outer surface of the root end region 61, the load transfer between the bushing 40 and the insert body 108 may be localised away from the root end region 61. In embodiments, an internal thread 66 or stud bolt engagement element, may be positioned in a root end region 61 of a bushing 40. In this way, as illustrated in FIG. 6a , load transfer between a hub connection element and the bushing 40, via engagement element 66, may be axially separated from load transfer between the bushing and the insert body 108. This may reduce peak loads experienced by the bushing 40. In embodiments, the root end region 61, axially offset from the body region 59, may exhibit a larger minimum outer diameter than the minimum outer diameter of the end region 61. This arrangement may ensure that, in embodiments where a thread 66 is axially offset from a textured region of a bushing 40, then the bushing 40 has a greater wall thickness in the region of the thread 66 than in the region of the textured outer surface. This, in turn, may improve the ability of the bushing 40 to withstand high levels of stress through the engagement element 66, perhaps especially at momentary high levels of stress.

Optionally therefore, the internal thread 66 in the bore 109 through the bushing 40 may be arranged within the end region 61. The end region 61 may have a smooth (un-grooved) cylindrical outer surface. The end region 61, offset from the body region 59, may be configured so that so that none of the grooves 68 encircle the internal thread 66. Offsetting the grooves 68 from the thread 66 in this way maximizes the wall thickness of the end region 61, making it crack-resistant. It also separates the bushing 40 into two, axially spaced, functional regions: the end region 61 and the body region 59. The end region 61 transmits loads between the stud bolt and the bushing 40, while the body region 59 transmits loads between the bushing 40 and the insert body 108, via a transition layer 102.

An effective wall thickness h (FIG. 6a ) of the bushing 40 may vary between a maximum, measured between the very outer extent of the bushing 40 e.g. at its root end region 61 or at a crest 69 between adjacent grooves and the inner wall of a bore 109, and a minimum extent between the grooves of an internal thread 66 and the grooves 68 of an undulating profile. A greater minimum wall thickness h at the threaded bore makes the area of high load transfer at an end region 61 more stress-resistant.

FIG. 7 is a side view showing three grooves 68 at a bushing 40 surface. FIG. 8 is a sectional view showing two of the grooves 68. As shown most clearly in FIG. 7, the grooves 68 and ridges 69 are annular rather than helical, so they each lie perpendicular to the length of the spindle 167, i.e. perpendicular to the axial direction of the bushing 40.

After a spindle 167 has been set up, a transition layer 102 may be built up around it as shown in FIG. 8. The transition layer 102 may comprise fibrous plies 98, each overlaid with a respective associated set of windings 80. In the illustrated example in FIG. 8, the transition layer 102 may comprise four fibrous plies 98, each overlaid with a respective associated one of four sets of windings 80. In FIG. 8, the four fibrous plies 98 are individually numbered 81-84, the ply 81 being the innermost ply. The number of fibrous plies 98 may however be two or three or four or five or more. Each ply 98 preferably has its own associated set of windings 80. In FIG. 8, The four sets of windings 80 are individually numbered 85-88, the innermost set of windings 85 being associated with the innermost ply 81. The transition layer 102 may be a continuous layer which terminates at each end of the spindle 167. In embodiments, the transition layer 102 may terminate where a last groove 68 meets the end region 61 of a bushing 40, as shown in FIG. 6a . Alternatively, a respective transition layer 102 may be applied such that it surrounds a respective bushing 40 at either end of said spindle 167.

The plies 98 may comprise sheets of fibrous sheet material 164, one sheet 164 being shown in FIG. 11b . By way of example the fibrous sheet material 164 may comprise glass fibre or synthetic material fibre such as high tensile polymeric material fibre. The term fibrous is used here although it may include fibrous sheets made of filamentary material such as glassfibre or other extruded type continuous filamentary material. The fibrous sheet material 164 may be selected from combinations of one or more of: unidirectional sheets, biaxial sheets (e.g. +45°/−45°) or tri-axial sheets (e.g. +45°/0°/−45°). By way of example, the fibrous sheet material 164 may be a nonwoven fabric made with unidirectional fibre layers stacked in different orientations and held together by through-thickness stitching. In embodiments, the fibrous sheet material 164 of an outer ply 98 may have a higher basis weight (g/sm) than the fibrous sheet material 164 of an inner ply 98. In a typical construction, the fibrous sheets 164 which make up the plies 98 may have a basis weight between approximately 400 g/sm and 1600 g/sm. By way of example, in one preferred embodiment, the first (innermost) ply 81 may comprise fibrous sheet material 164 in the form of a 600 gram per square meter (g/sm) biaxial sheet (+45°/−45°), while one or more of the other plies 98 may comprise fibrous sheet material 164 in the form of biaxial sheets (+10°/−10°) with a higher weight, such as for example 1200 g/sm. Alternatively, some or all of the plies 98 may be made up of multiple sheets—for example the first (innermost) ply 81 may comprise two sheets with each sheet having a basis weight of 300 g/sm.

FIGS. 11a, 11b and 12 show a tool for forming the transition layer 102. The spindle 167 is rotatably mounted between a pair of bearings 130. First, as indicated in FIG. 11b , an innermost fibrous ply 81 is wound onto the spindle 167 by unwinding it from a spool 136 of fibrous sheet material 164 and rotating the spindle 167 by at least one complete turn. In embodiments, two or more complete turns may be preferred so that the innermost ply 81 is formed from multiple layers of the fibrous sheet material 164 forming a spiral. Initially the ply 81 has a cylindrical profile as shown in FIG. 11b and covers the grooves 68 and the core 62. After wrapping a length of the fibrous sheet material 164 around the spindle 167, the sheet material 164 may be cut, leaving the spindle 167 completely wrapped by at least one turn of the fibrous sheet material 164.

Next, as shown in FIG. 11a , the spindle 167 is rotated while a line of filamentary material 131 such as filamentary tow is fed from a spool 132. A typical filamentary material used for this purpose may be e.g. carbon fibre or glassfibre or high-tensile polymeric material. Examples include 12K carbon fibre tow. “12K” denotes the fact that the filamentary material 131 is a bundle of 12,000 filaments, although other gauges of tow may be used such as e.g. anywhere between 2K and 40K. Initially the spool 132 may be positioned in line with a first groove 68 at or near an end of the bushing 40. For example, the spool 132 may initially be positioned at or nearby an end region 61 of the bushing 40. Thereafter, the spindle 167 is rotated so that the filamentary material 131 is wound into a first groove forming a winding 80 around the innermost ply 81 and binding that portion of the ply 11 into a groove 68 of the bushing. The number of turns of the spindle 167 at this stage determines the number of windings 80 of filamentary material 131 in the groove 68. For example, one or two or three or four or more turns of the spindle 167 may be made, generating correspondingly one or two or three or four or more windings 80 in the groove 68. Preferably, the spool 132 may be moved along a track 134 until the filamentary material 131 is in line with a next groove 68. The spindle 167 continues to be rotated as the spool 132 of filamentary material 131 moves incrementally between the adjacent grooves 68, so that an angled connecting section 70 of the filamentary material 131 rides over the ridges 69 between the grooves 68 as shown in FIG. 7 and connects together windings 80 in adjacent grooves 68. The process then continues groove-by-groove 68 until a first set of windings 80 is in place. In FIG. 8, the first set of windings is shown with the number 85 and has two windings per groove. The filamentary material 131 is then tied off at each end, for instance by wrapping it over itself.

The illustration at FIG. 8 shows how a first set of windings 85 draws an associated first ply 81 into the grooves 68 of the bushing 40 so that it deforms from a cylindrical profile to adopt the wrinkled or corrugated profile shown in FIG. 8, including circumferential annular corrugations which are anchored into the grooves 68 by the first set of windings 85 as shown in FIG. 8.

Next, a second fibrous ply 98, shown in FIG. 8 with numeral 82, is wrapped around the spindle 167 and a second associated set of windings 80, shown in FIG. 8 with numeral 86, is wrapped around it, binding or anchoring it into the grooves 68—this time with e.g. four windings 80 per groove 68 rather than the two as illustrated in FIG. 8 over the innermost ply 81. The second set of windings 86 draws the associated second ply 82 into the grooves 68 so that the ply 82 adopts the undulating or corrugated profile shown in FIG. 8, including circumferential annular corrugations which are anchored into the grooves 68 by the windings 86. The process may be repeated to complete the transition layer 102, for example by adding further plies 98 (shown in FIG. 8 with numerals 83 and 84) bound in place by additional associated sets of windings 80 (shown in FIG. 8 with numerals 87 and 88).

The sets of windings 80 (shown in FIG. 8 as four sets of windings 85-88) run along the grooves 68 and alternate with the fibrous plies 98 (shown in FIG. 8 as four fibrous plies 81-84) which overlie the grooves 68. The innermost plies 98 may have significantly undulating profiles including circumferential annular corrugations which are anchored into the grooves 68 by their associated windings 80. This anchoring provides a strong interface which resists the bushing 40 being pulled out axially from the finished insert body 108, and is fatigue resistant. The fibrous sheet material 164 making up the plies 98 may be wrapped around the bushing 40 in such a way as to apply a fibre direction running across the grooves at an oblique angle to the grooves 68 such as 45°. Additionally or alternatively, the fibrous sheet material 164 may be wrapped around the bushing 40 such as to apply a combination of fibre directions running across the grooves 68. In this way, for example, one ply 98 may exhibit a fibre direction at 45° while another ply 98 may exhibit a fibre direction at 90° or 60° or 75° etc. As a result of the tightly wound filamentary material 131 making up windings 80 around the fibrous sheets 164, the plies 98 running across the grooves 68 thereby adopt a corrugated shape, or corrugations, as they are anchored into the grooves 68 by the windings 80.

The corrugations progressively reduce in amplitude from ply-to-ply in a direction away from the bushing 40 surface so that the corrugations in e.g. a relatively outer ply 98 may be relatively shallow and, unlike the first, second and third plies 98 (shown in FIG. 8 as innermost plies 81-83), the corrugations of a relatively outer ply such as a fourth ply 98 (shown in FIG. 8 with numeral 84) or subsequent ply 98 may hardly extend into the grooves 68. In embodiments, the number of windings 80 overlying a ply 98 may progressively increase from one ply to a subsequent ply in a radial direction away from the bushing 40 surface. In optional embodiments, the outermost fibrous ply 98 of the transition layer 102 (shown as ply 89 in FIG. 8) may be wrapped around an outermost corrugated ply 80 (shown as ply 84 in FIG. 8) in such a way as to maintain a cylindrical, un-corrugated profile because no windings 80 are applied around it. Optionally this cylindrical outermost ply 90 may extend to cover the end region 61 of the bushing 40, unlike the corrugated plies 81-84.

The windings 80 may be formed by rotating the spindle 167, each rotation of the spindle 167 forming a single winding 80. The number of windings 80 per groove 68 for each set of windings may increase in a radial direction away from the bushing 40 surface. So the sets of windings 80, illustrated in FIG. 8 with numerals 85-88, may have two, four, six and eight turns per groove 68 respectively. Accordingly, the number of filaments per groove 68 may thereby correspondingly increase in a radial direction away from the bushing 40 surface. By way of example, with two windings 80 of a 12K filamentary tow over a given ply 98 in a single groove 68, there may be a 24,000 individual filament count (e.g. the innermost, first set of windings 85 shown over innermost ply 81 in FIG. 8). This may increase to e.g. 96,000 filaments per groove 68 over a subsequent or outermost ply 98 (e.g. the fourth set of windings 88 over the fourth ply 84 shown in FIG. 8).

As mentioned above, the circumferential grooves 68 and ridges 69 are preferably annular. The term “annular” is used herein to denote a closed or endless non-helical shape, which may or may not be circular. So there may be multiple unconnected annular grooves 68, rather than connected grooves which would collectively form a single helical external thread which runs along the full length of the body region 59 of the bushing. The annular groove shape enables multiple windings to be wrapped into each groove with a single pass of the spool 132. In an alternative embodiment, a helical external thread may be used (not illustrated), but in this case multiple passes of the spool 132 along an entire grooved body region 59 must be used if it is required to wrap multiple windings 80 into the external thread.

The outer surface of the bushing 40 has a sectional profile across the grooves 68 and ridges 69 with a series of crests and troughs as shown in FIGS. 6a, 6c and 8. The crests and troughs may be triangular as in FIG. 6a , or with flat crests as in FIG. 8, but in FIG. 6c a more preferred sinuous sectional profile is shown. In this case the sectional profile has rounded convex crests (corresponding with the ridges 69). The rounded crests may for example have a radius of curvature of about 4-8 mm, optionally 4-6 mm, optionally 4 or 5 mm, optionally about 4.54 mm. The sectional profile also has rounded concave troughs (corresponding with the grooves 68) with a radius of curvature of about 4-8 mm, optionally 4-6 mm, optionally 4 or 5 mm, optionally about 4.54 mm. The illustrated grooves 68 have a depth A and are separated by a pitch P. In the case of FIG. 6c the pitch P is 10 mm, and the depth A is 1.5 mm. So the grooves are relatively shallow and the ratio A/P is low—in this case about 1/6.7. This low ratio makes the walls of the grooves less steep which make it easy to anchor the fibrous plies into the grooves—particularly the innermost ply 81 which must closely follow the sinuous profile of the bushing as shown in FIG. 8. Other values of the pitch P and depth A may be used.

FIG. 9 shows an alternative transition layer 102 a, formed using windings alone. In embodiments, an initial set of windings 90 of filamentary material 131 which may run at a first angle to the length direction of the bushing 40. By way of example, the initial set of windings may be wound at a first angle of 90° to the length direction of the bushing 40. Further windings 91 of filamentary material 131 may be wound around the bushing 40 at a different angle, e.g. 15°, 30°, 45°, 60° or 75°. In embodiments, the filamentary material windings 90, 91 may comprise glassfibre or carbon fibre tow. FIG. 10 shows a further alternative transition layer 102 b also formed using windings alone. In the case illustrated in FIG. 10a single set of windings 100 is arranged over the grooves 68, at a given winding angle to the bushing 40, with no additional overlying windings 91. By way of example the filamentary material 131 of the illustrated windings 100 may be glass or carbon fibre. These may run at 90° to the length direction of the bushing 40.

In the method described above, the sheet material 164 forming each ply 98 of the transition layer 102 may extend almost the full length of the spindle, up to an end region 61 of each bushing 40. In other embodiments (not shown) each ply 98 may be formed from multiple sheets laid up side by side, or it may be formed by winding a narrow strip or tape of fibrous material onto the spindle 167 thereby to cover the bushing 40 and all of or part of the core 62 in a spiral.

In the example described above, the windings 80 may optionally be formed from filamentary material 131 in the form of tow, such as carbon tow. In alternative embodiments, perhaps for cost reasons, the filamentary material 131 may be replaced by a twisted fibrous yarn (not shown) provided the requisite level of tension can be applied to it and maintained. Preferably, the bushing may be made from a metal, preferably steel or titanium. In one embodiment, carbon filament windings are arranged around the metal bushing and around fibrous plies such that the carbon filaments are not in contact with the metal bushing.

Once the transition layer 102 has been formed as described above, two or more fibrous battens 148 may be positioned around the transition layer 102 to form the insert body 108. These battens may preferably give the insert body 108 a square or trapezoidal cross-section. A batten 148 can have different forms. These battens may include for example: a pultruded preform 150 as shown in FIG. 13, or assemblies of pultruded glass fibre rods 160, 170 as shown in FIGS. 14 and 15 respectively. Note that in FIG. 13, a bushing 40 is illustrated, while the transition layer 102 is not shown. The pultruded glassfibre rods may in particular be provided in a single gauge, as shown for example in FIG. 14 or in a mix of gauges, as shown in FIG. 15. In all cases, the battens 148 allow to generate a desired cross-sectional shape of the insert body 108 prior to a wrapping and/or moulding step for further forming the insert 105. The longitudinally arranged battens 148 also give structural strength to the insert body 108. In embodiments the battens 148 may be porous and capable of being infused by resin. In one embodiment (not shown) the battens may be formed by placing lengths of rope alongside the bushing 40, preferably along and adjacent to the transition layer 102.

As shown in the example of FIG. 13, the preforms 150 may have a deltoid cross-section with a concave cylindrical inner face 151. The deltoids may approximately conform to the convex cylindrical outer contour of a transition layer 102 (see e.g. FIG. 6b ), and a pair of outer faces 152 which meet at a convex or outer corner or edge 153. In embodiments, a preform 150 may be made from pultruded, fibrous material in a resin matrix. Alternatively, in embodiments, a preform 150 may comprise a “dry” pultruded fibre material containing binder material but no resin, so it remains porous. The “dry” fibre material may be pultruded by coating fibres in the binder material, or by adding powdered binder material to the fibre material, and then pulling them through a heated die having the required deltoid cross-section. The binder material holds the fibres together so the preform 150 retains the deltoid cross-section. In the context of the deltoids, or preforms, the term “fibre” is intended to designate filamentary material such as continuous filamentary material such as glassfibre or carbon fibre or other extruded filamentary material such as filamentary polymeric material.

In FIG. 13 or FIG. 6b , the insert is shown having four fibrous battens 148 in the form of pultruded preforms 150. Each preform 150 preferably has a deltoid cross-section with a concave inner face 151 which lies adjacent, and may preferably contact, the transition layer 102. Note that for purposes of illustration, the transition layer 102 is not shown in FIG. 13, to enable the grooved outer surface of the bushing to be seen. Note also that in this example, the grooves in the outer surface are shown almost up to the root end of the bushing, unlike in FIG. 6a in which the end region 61 of the bushing has no grooves.

The pair of outer faces 152 meet at an external corner 153 of the deltoid preform 150. Each preform 150 may have an identical cross-section. In this way, the deltoid preforms 150 give the insert body 108 a square cross-section. In the alternative example of FIG. 14, the insert body 108 may have only two battens 148, each shaped in the form of a half hourglass shape, having two deltoid lobes.

A plurality of pultruded rods 160 or 170 may be aggregated or assembled together into an approximate deltoid shape. In an embodiment, as shown in FIG. 14, pultruded rods 160 which may be of a same gauge may be aggregated to form longitudinally extending deltoid shapes. These aggregated rods 160 may then be laid alongside a wrapped bushing 40 to generate an insert body 108 having the desired cross-sectional shape and having the desired structural properties.

In further embodiments (not shown) lengths of rope may be used to form the battens 148 instead of pultruded preforms 150 or rods 160, 170. Such rope may be porous. Lengths of rope may be positioned approximately as illustrated in the embodiment of FIG. 14, although it may be preferred to use a single larger gauge rope which, being compliant, may be formed into a deltoid shape, occupying the corresponding space along a wrapped bushing 40.

The use of four separate fibrous battens 148 (as in FIG. 13) may be preferred over two battens 148 as in FIG. 14, since they can be moved about independently to better conform around a bushing 40 and provide a “wedging” effect which can improve consolidation in the final moulded product.

FIG. 15 illustrates a further alternative deltoid fibrous batten 148, in this case formed by an assembly of porous glass fibre rods 170 having varying circular cross-sectional areas so they form the required deltoid cross-section. The rods 170 can be stabilised by being attached to a mesh 171 wrapped around the transition layer, or by placing them in a former and bonding them together at discrete locations. The cross-sections approximate to a deltoid shape, so the battens give the part a square cross-section. According to the embodiment illustrated in FIG. 15, a large gauge pultruded rod 170 may be positioned at a longitudinally extending corner position of an insert body 108. Smaller gauge pultruded rods 170 may be positioned in flank regions adjacent the corner rod 170. In some embodiments, flanking rods may also be of varying gauge. Flanking rods 170 may decrease in cross sectional size in a direction away from a larger gauge corner rod 170.

An advantage of using ropes or rods 160, 170 for the battens 148, compared with the use of pultruded preforms 150, is that the ropes or rods 160, 170, being stock products, are available at low cost and do not require a bespoke pultrusion die.

The battens 148 may extend along the full length of the bushing and core 62, covering not only the transition layer 102 but also the end region 61 of the bushing. Alternatively, the battens 148 may terminate at the end of the body region 59 where the body region 59 meets the end region 61. Accordingly, one-piece end caps (discussed below with reference to FIG. 31) may be fitted over the end regions 61, the end caps having the required square or trapezoidal outer profile of the insert body 108.

The cylindrical profile of the outermost ply 89 of the transition layer 102 ensures a smooth connection surface to interact with the deltoid battens 148 described above. After the battens 148 have been fitted, an outer shell layer 186 (shown in FIG. 6b ) comprised of sheets of fibrous sheet material 164 may be wrapped around the assembly, thereby to bind together the assembly of the battens 148 and the wrapped bushing 40. The outer shell layer 186 may thereby form an outside region of the insert body 108. The fibrous sheets 164 of the outer layer 186 may comprise unidirectional fibres or bi-axial or tri-axial fibre layers. The fibrous sheet material of the outer shell layer 186 may optionally have a higher basis weight than one or more of the plies 98 of the transition layer 102 around the bushing 40. Alternatively, the fibrous sheet material of the outer shell layer 186 may optionally be of a same material or type as one or more of the plies 98 of the transition layer 102 around the bushing 40. Optionally, the fibrous sheet material 164 of the outer shell layer 186 may be applied by unwinding the material 164 from the spool 136 and rotating the spindle 167 by a required number of turns. In embodiments, a single turn may be applied although it may be preferred to apply two or three or more turns of the sheet material 164 to make up the outer shell layer 186. Finally, the outer shell layer 186 may be secured in place by winding filamentary material 131 around it, as shown in FIG. 12. The filamentary tow 131 around the outer shell layer 186 may be the same as or of a different type than the filamentary material 131 of the windings 80 over the plies 98 of the transition layer 102. Optionally, 12K carbon fibre tow may be wound around the deltoid battens 148 before the sheets of the outer shell layer 186 are applied, in order to hold the battens 148 to the bushing 40 and the core 62.

Once the winding process of fibrous sheet material 164 and filamentary material 131 around the bushings 40 and core 62 has been completed, the final assembly 120 shown in FIG. 12 may then be removed from the bearings 130.

As shown in FIG. 6a , the bushing 40 may have a plug 75 blocking its internal bore 109. Optionally, the plug 75 may be positioned between the frustoconical recess 65 and the bore 109. The plug 75 may prevent matrix material from flowing from the recess 66 into the bore 109 during the infusion process. Optionally, the plug 75 may be integral with the bushing. Alternatively, the plug may be added as a separate element in the bore 109.

Each pultruded preform 150 in the assembly 120 may comprises a “dry” fibre material containing binder material but no resin, so it is porous and becomes infused with epoxy resin in the infusion mould. In an alternative embodiment, each pultruded preform 150 in the assembly 120 may be supplied as a cured fibre-reinforced composite material—such as a fibrous material in a cured vinyl ester resin.

After it has been moulded in the mould cavity and cured, the intermediate product shown in FIGS. 17-20 can be removed from the infusion mould. The intermediate product of FIGS. 17-20 is referred to below as a blank 190. The walls 182, 183, 185 of the mould cavity may give the blank 190 a desired outer profile, an example of which is shown in FIGS. 17-20. It should be noted that in FIGS. 17-20 and throughout this specification, the draw angle, that is to say the angle of convergence of the side faces 343, 344 of the blank 190, at its respective end faces 312 a, 312 b is greatly exaggerated, for clarity. In practice, the deviation from a right-angle may be of the order of one or two degrees, between both side faces 343, 344.

The purpose of making inserts 105 by the method of placing two bushings 40 at either end of a longitudinal core material 62 to form a spindle 167, is to optimise and rationalise the forming process for the inserts 105. The process is optimised because it allows two inserts 105 to be made from a single blank 190, by dividing the double-ended blank 190 into two parts, to form two inserts. In other words, a single moulding or forming process of a blank 190 may be used to make two inserts 105. When using the RTM process to form the blanks 190, a problem arises in that it is difficult to obtain the optimal shape of the inserts 105 by this method. It is possible to obtain a rectangular prism by RTM moulding, although it can be difficult to extract a parallel-sided, moulded prism from its RTM mould without using a removable mould insert, in the form of a removable side wall portion which may be tapered to allow its removal from the mould together with the moulded blank. The moulded blank may then be released from the removable mould insert outside the mould. The same technique may be used when moulding parts with undercuts. But using a removable wall portion of a mould creates difficulties when working with resin infusion techniques, because the resin tends to glue the supposedly removable mould elements together, or to clog up the separable mould elements. In any case, even if a parallel-sided rectangular prism shape were moulded to form a double-ended blank 190, the inserts 105 generated from such a blank would need to be machined to a slightly trapezoid shape in order to enable the creation of a circular arrangement of inserts 105 around a blade root, when these inserts 105 are butted-up side by side as in FIG. 4. It is possible to mould a prism shape in the form of a trapezoid, whose sloping sides would allow removal from an RTM mould. But if a trapezoid prism is to be divided into two identical inserts 105, the division can only be by way of a bisection of the lengthwise extent of the blank 190. In the case of root inserts 105, this generates a suboptimal shape for the manufacturing process and for the laid up inserts 105 in a blade root 20. In particular, it is desirable to provide inserts which exhibit a tapering portion, tapering down in a direction away from the root face of a wind turbine blade. This tapered shape of an insert 105 allows a more gradual load transfer between an insert 105 and the composite material of the wind turbine blade shell 27. The creation of a tapered insert from a double-ended blank 190 preferably requires a diagonal cut to be made through the blank 190, dividing the blank 109 into two identical inserts 105. When a blank 190 has the shape of a rectangular prism, such a diagonal cut generates two identical inserts 105. On the other hand, if the blank has the shape of a trapezoid, the two inserts 105 generated from a diagonal sectioning cut will be non-identical, as in a left and a right shoe, or such like. This means that when forming a circle from the tapered trapezoid inserts 105 arranged side-by-side, one set of inserts will leave the tapered faces oriented in a direction opposite to the orientation of the tapered faces of the other set of inserts. In other words, one set of inserts would be unusable. In either case, whether moulding rectangular or trapezoidal blanks 190, an additional machining step would be required to be performed on the sectioned inserts 105 in order to generate inserts 105 which can be fitted together to create a circle of inserts 105 having a consistent geometry. In order to overcome this problem, it is suggested to generate the blank 190 in the form of a double trapezoid shape. This double-trapezoid shaped blank 190 allows the creation of two identical, tapered inserts 105 each having a slightly trapezoid cross section, merely by diagonally sectioning the blank 190. Such inserts 105 may be laid-up at a root portion 20 of a wind turbine blade 18 without further machining, and preferably without requiring the insertion of wedge-shaped shims between adjacent inserts 105. A double-trapezoid blank 190 has an advantageous shape, allowing it to be bisected into two identical or near-identical inserts 105. Aspects of the present invention may include a process for making such a blank 190, which process is adapted in certain ways, as well as aspects of the blank itself.

FIG. 32 shows a composite, elongate blank 190 having an elongate blank body 300. The blank body 300 extends longitudinally about a longitudinal axis (not drawn) between trapezoid end faces 312 a, 312 b. The illustrated end faces include a first end face 312 a and a second end face 312 b. Each end face 312 a, 312 b is bounded by edges which define its trapezoid shape. A first end face 312 a comprises two opposing parallel edges: a fist, minor end edge 361 a and a second, major end edge 362 a. The first end face 312 a comprises two non-parallel opposing side edges or equal or near-equivalent length: a side, third edge 363 a and a side, fourth edge 364 a. A second end face 312 b comprises two opposing parallel edges: a major, first end edge 361 b and a minor, second end edge 362 b. The second end face 312 b comprises two non-parallel opposing side edges: a side, third edge 363 b and a side, fourth edge 364 b. The blank body 300 has four principal, longitudinal, peripheral faces, including a first peripheral face 341, a second peripheral face 342, a third peripheral face 343 and a fourth peripheral face 344. Each said peripheral face 341-344 extends in a longitudinal direction of the blank 190. Each said longitudinal face 341-344 connects corresponding pairs of side edges 361 a and b; 362 a and b; 363 a and b; 364 a and b. Said first peripheral face 361, joins a minor, first end edge 361 a with a major second end edge 361 b; said second peripheral face 362, joins a major, first end edge 362 a with a minor, second end edge 362 b; said third peripheral face 363, joins a side, third edge 363 a of a first end face 312 a with a side, third edge 363 b of a second end face 312 b; said fourth peripheral face 364, joins a side, fourth edge 364 a of a first end face 312 a with a side, fourth edge 364 b of a second end face 312 b. In the embodiment illustrated in FIG. 32, the blank body 300 defines a transition portion of the blank 190, along which the cross section of the blank 190 transitions from a trapezoid shape at a first end 312 a of the transition region to an inverted trapezoid shape at a second end 312 b of the transition portion 200. In the embodiment of FIG. 32, the transition portion 200 extends between the end faces 312 a, 312 b of the blank 190. In other embodiments, a transition portion 200 may begin and end longitudinally inboard of said end faces 312 a, 312 b, between end portions 192 a, 192 b of the blank body 300. The first and second peripheral faces 341, 342 of the blank 190 may be planar; preferably planar and parallel; preferably also flat. The side, third face 343 and the side, fourth face 344 may be predominantly, although not strictly planar. The side, third face 343 and the side, fourth face 344 may be predominantly planar and slightly curved or arcuate. Parts of the side faces 343, 344 may be planar. In particular, the side faces 343, 344 may comprise more than one planar facet. The transition portion 200 may have a variable cross section along its length. The transition portion may have a generally quadrilateral cross section along its length. A cross-section of the transition portion 200 may include straight, parallel upper and lower edges and non-parallel lateral edges. The lateral edges of a cross-section across the transition portion 200 may be partly concave or slightly concave. Each end portion 192 a and 192 b may comprise a respective embedded bushing (not shown). The trapezoid cross section of the first end portion 192 a is inverted relative to the quadrilateral cross section of the second end portion 192 b. The upper and lower faces 341, 342, of the blank body 200 may be parallel and planar trapeziums, which taper in opposite directions. The side faces 343, 344 may be non-planar, continuously curved surfaces which twist along the length of the blank. The blank 190 shown in FIG. 32 may be bisected into equal parts, in particular to form two equally dimensioned inserts 105. A bisection plane may pass transversely through the blank 190. The bisection plane may intersect diagonally with the side faces 343, 344. The bisection plane may intersect at a straight, transverse line with the upper and lower faces 341, 342. Each insert may extend from a root face end 232 to an embedment end 236.

In an alternative embodiment, and referring to FIGS. 17-20, the blank 190 preferably has the approximate shape of a prism. The blank 190 in addition to its transition portion 200 may also comprise a pair of end portions 192 a and 192 b being a first 192 a and a second 192 b respective end portion. Each end portion 192 a and 192 b may contain a respective bushing 40. Each end portion 192 a or b preferably has four peripheral faces which meet at four edges or corners to preferably form a slightly trapezoidal cross-section. Thus, for example, the faces of the first end portion 192 a may comprise a respective first end portion major face 194 a; a first end portion minor face 196 a; and a pair of first end portion side faces 198 a. On the other hand, the faces of the second end portion 192 b may comprise a second end portion major face 194 b; a second end portion minor face 196 b; and a pair of second end portion side faces 198 b. Note that the degree of convergence of the angle subtended by the end portion side faces 198 a and 198 b is exaggerated in FIGS. 17-23 to emphasise the trapezoidal shape of that part of the blank 190. Preferably all the peripheral faces of the end portions 192 a, 192 b extend parallel to a longitudinal axis through said blank 190.

At a respective first or second end of the blank 190, each said major face 194 a or b of the blank 190 is wider than its associated minor face 196 a or b. As shown most clearly by comparing FIG. 21 with FIG. 23, the trapezoidal cross section of the first end portion 192 a of the blank 190 is inverted relative to the trapezoidal cross section of its second end portion 192 b. So the major face 194 a of the first end portion 192 a (shown in FIG. 23) is at the blank's lower face 342, whereas the major face 194 b of the second end portion 192 b (shown in FIG. 21) is at its upper face 341. Similarly, the said minor face 196 a of the first end portion 192 a is at the blank's upper face 341, whereas the said minor face 196 b of the second end portion 192 b is at its lower face 342.

In embodiments, a transition portion 200 may extend between the two end portions 192 a, b of the blank 190. As mentioned above, each end portion 192 a and 192 b may contain a respective bushing 40 and the trapezoidal cross-section of each end portion 192 a, b preferably does not vary along the longitudinal direction of the blank—in other words each end portion has a parallel-sided prismatic shape. The transition portion 200, on the other hand, has a cross-sectional shape which preferably varies continuously along the longitudinal direction of the blank. Therefore, in the embodiment of FIGS. 17-23 the transition region 200 defines that part of the blank 190 along which there is a shape transition between the mutually inverted trapezoidal cross-sectional shapes of the first portion 192 a and the second portion 192 b.

The transition portion 200 may comprise a pair of opposing side faces 343, 344, each one of which meets a respective end portion side face 198 a and 198 b at each of the end portions 192 a and 192 b. One of the side faces 343 of the transition portion 200 is shown in FIG. 17, and the corresponding opposite side face 344 is shown in FIG. 18. Each side face 343, 344 of the transition portion 200 of the blank 190 may be smooth, continuous. Alternatively, each said side face may comprise multiple planar facets. For example a side face 343, 344 of a transition region 200 may have two planar triangular facets 202 a,b. According to this embodiment, top facets 202 b may meet bottom facets 202 a at a diagonal edge or corner 204. The blank 190 of FIG. 17 may be cut into a matching pair of inserts by cutting along a diagonal edge 204 across a side face 343, 344.

The transition portion 200 has a preferably planar upper face 206 b shown from above in FIG. 19 which meets the second end portion major face 194 b and the first end region minor face 196 a of the end portions 192 a, 192 b; and a preferably planar lower face 206 a shown from below in FIG. 20 which meets the second end portion minor face 196 b and the first end portion major face 194 a of the end portions 192 a, 192 b.

FIGS. 21-23 show how the cross-section of the blank 190 may change along its length. At the mid-point, the cross-section has a waisted profile shown in FIG. 22 with the diagonal edge or corner 204 at a mid-point between the upper surface 206 b and a lower surface 206 a.

An insert 105 shown in FIGS. 24-26 will now be described, using the same reference numbers as the blank 190 from which it may be cut. The illustrated insert 105 extends from a root face end 232 to an embedment end 236. It has a root end portion 192 a with faces which form a trapezoidal cross-section, the faces comprising a major face 194 a, a minor face 196 a, and a pair of angled side faces 198 a. The major face 194 a is wider than the minor face 196 a. When it is integrated into a wind turbine blade 20, the major face 194 a is on the outside of the ring of inserts 105, and the minor face 196 a is on the inside. The insert 105 also has an extension portion 200 a, formed from the lower half of the transition portion 200 of the blank 190, which tapers inwardly in both height and width as it extends away from the end portion to a pointed tip 224 a. The extension portion 200 a has an outer face 206 a (shown in FIG. 25) which meets the major face 194 a of the end portion; a cut inner face 226 a (FIGS. 24 and 26) which meets the minor face 196 a of the end portion at an edge; and a pair of triangular side faces 202 a. The triangular side faces 202 a may be formed from the lower facets of the side faces 343, 344 of the blank 190. Although the insert 105 illustrated in FIG. 24 is shown with an end region 192 a which has all peripheral sides parallel to its longitudinal axis, which may also be parallel to a longitudinal axis of a bushing 40 embedded in it.

As shown in FIG. 25, the insert 105 may exhibit a maximum width dimension W1 at its root face end 232, larger than a maximum width dimension W2 at its embedment end 236. The insert may reduce uniformly in width from W1 to W2 as it extends away from the root end face 323, towards the embedment end 236, at its tip 224. Alternatively, the outer face 206 a of an extension portion 200 a may have have a width which reduces uniformly from W1 to W2 as it extends away from the end portion 192 a to the tip 224 a.

The insert 105 has a height H1 between its upper and lower faces 341, 342. The height H1 at a root face end 232 may progressively reduce to zero at an embedment end 236. In alternative embodiments, as shown in FIG. 26, the height H1 at an end portion 192 a, between outer and inner faces 206 a, 226 a may reduce uniformly from H1 to zero as it extends away from the end portion 192 a to the tip 224 a of the extension portion 192 a.

As described above with reference to FIG. 4, an insert 220 a may be integrated into a blade root 20 between glass fibre composite walls 41 and 42 with its outer faces 194 a, 206 a bonded to the outer composite wall 41 and its inner faces 196 a, 226 a bonded to the inner composite wall 42. The angle of taper between the outer and inner faces 206 a, 226 a of the extension portion of the insert may lie between 2 degrees and 20 degrees; preferably between about 2 degrees and 15 degrees; preferably between about 2 degrees and 10 degrees; preferably between about 3 degrees and 10 degrees; preferably between about 4 degrees and 8 degrees. In one embodiment, the angle of taper between the outer and inner faces 206 a, 226 a of the extension portion of the insert may be about arctan(0.1)—i.e. about 6° (note that this angle of taper is exaggerated in FIG. 26). This low angle of taper means that the plies of the inner composite wall 42 can be dropped off gradually. This may result in a low stress concentration when loads are transferred between an insert 220 a and a blade 20. For example, about five or ten or more plies may be dropped off along the length of the angled inner face 226 a.

Preferably, the assembled elements for making a blank 190 may be placed in a resin transfer moulding (RTM) infusion mould, an example of which is shown in FIG. 16. The illustrated infusion mould 250 may comprise a base 180 with opposing side walls 182, a floor 185, and a lid 181, which together define a mould cavity. The lid 181 may have a moulding top surface 183 opposite the floor 185. FIG. 16 shows the two parts 180, 181 of the mould 250 containing an insert assembly 120. After the lid 181 is fitted, a matrix material (such as epoxy resin) is injected into the infusion mould 250 so that the matrix material infuses though the porous fibrous material forming the transition layer 102, around or through the battens 148 and the outer shell layer 186. The assembly 120 thereby adopts the profile of the mould cavity. Still with reference FIG. 16: the floor 185 of the base 180 and the moulding surface 183 of the lid 181 may contact and mould the side faces 343 and 344 of the blank 190. The side walls 182 of the base may contact and mould its upper face 341 (or including 194 a, 206 a, 196 b) and lower face 342 (or including 196 a, 206 b, 194 b). Note that the angles of the upper and lower surfaces 183, 185 may be exaggerated in FIG. 16 for purposes of illustration.

In the finished blank 190, the upper and lower faces 341, 342 may be parallel, in fulfilment of the trapezoidal cross-section of the end portions of a blank 190. However, for moulding the blank in a recessed mould having fixed, opposing side walls 182 and a fixed floor surface 185, per FIG. 16, the side walls 182 of the base 180 may need to be formed with a small draw rather than being parallel in order to allow removal of the moulded blank 190 from the mould base 180. Optionally the blank 190 may then be machined to remove the excess material caused by the small non-parallel, divergent draw, so that the upper and lower faces 343, 344 are made parallel for the cross-sections of the end portions 192 a,b to become precisely trapezoidal.

The four battens 148 may preferably be similar or identical, so the outer profile of the assembly 120 may be square rather than trapezoidal as it is fitted into the infusion mould 180 as shown in FIG. 16. Optionally a twist or plait of glass fibre roving may be placed in the lower corner 188 of the mould base 180 at the wide part of the trapezoid section, preferably under any sheets of undirectional glass fibre which make up the shell 186. Similarly, a twist or plait of glass fibre roving may be placed in the upper corner 189 at the wide part of the trapezoid section. The glass roving may be placed under the one or more sheets of undirectional glass fibre sheet material which make up the shell 186. These twists/plaits give the assembly 120 a slightly trapezoidal shape prior to moulding, and encourage greater conformity into the mould corners.

Once the blank 190 has been cured and removed from the mould 250, it may be cut diagonally into two equally dimensioned parts. The provision of a blank 190 with a double-trapezoid shape as described herein, wherein one trapezoidal end 192 a is inverted in relation to the other trapezoidal end 192 b, ensures that the two inserts 105 which are formed as a result of bisecting the blank 190 are of equal dimensions and substantially identical. In embodiments, cutting may be carried out along the diagonal edges 204 to provide a matching pair of inserts 105. One of the inserts 105 of the matching pair is shown in FIGS. 24-26.

An alternative infusion mould 250 for infusing and shaping the blank 190 from an assembly 120 is shown in FIG. 27. The mould 250 comprises first and second mould parts which meet at a split line 259: namely a base 251 and a lid 252. The base 251 has a pair of moulding faces 254, 255 and the lid 252 has a pair of moulding faces 256, 257.

Unlike the infusion mould of FIG. 16, each mould part 251, 252 contacts and moulds a respective side face 343, 344 of the blank 190. So the moulding face 255 of the base may contact one side face 343, and the diagonally opposite moulding face 256 of the lid may contact the other side face 344.

By way of example, the lower face 342 of the blank 190 may be contacted by the moulding face 254 of the base 251; and the upper face 341 of the blank 190 may be contacted by the diagonally opposite moulding face 257 of the lid 252. The base 251 may thereby mould both the minor face 196 b of the second end portion and the major face 194 a of the first end portion, and the lid 252 may mould the major face 194 b of the second end portion and the minor face 196 a of the first end portion.

The split line between the base 251 and the lid 252 substantially coincides with a diagonal of the quadrilateral cross-section of the blank 190, which is its maximum cross-sectional dimension. This diagonal split mould arrangement thereby has an intrinsic draw angle which enables the cured blank 190 to be removed from the mould in its final shape—not requiring any machining after it has been removed from the mould, unlike the arrangement of FIG. 16. The diagonal split mould thereby removes a need for additional machining of the blank or inserts before use in a blade root 20 lay-up.

The mould cavity of the diagonal split mould 250 of FIG. 27 therefore preferably has a trapezoid cross-section at each end, so the end portions of the moulded and cured blank 190 have the described trapezoid cross-sections. In a further alternative moulding arrangement, the mould cavity of the diagonal split mould 250 of FIG. 27 may have a square or rectangular cross-sectional shape rather than double-trapezoid. The moulded and cured blank may then be then machined to give it the double-trapezoid shape shown in FIGS. 17-23 before it is cut diagonally to provide the matching pair of inserts, although this variant is not preferred.

FIG. 14 shows a two-batten arrangement in which each batten 148 optionally has a pair of lobes. The lobes may be formed from pultruded fibrous preforms 150 or e.g. formed by glass fibre rods 160. FIGS. 28 and 29 show similar lobed batten arrangements formed from pultruded preforms 150. According to an embodiment illustrated in FIG. 28, the two preforms 150 may have first and second lobes joined by a connection portion. The lobed battens 148 may be arranged on opposite sides of an assembly 120, to make up part of the body 108 of an insert 105. Still alternatively, as shown in FIG. 29, the two-lobed battens 148, in the form of preforms 150 may be arranged on the top and bottom of the assembly 120. Each lobe preferably has a deltoid cross-section with a concave inner face which contacts the transition layer 102, and a pair of outer faces 261 which meet at a convex corner 262.

The battens 148 may extend along the full length of a bushing and core 62 up to the root end of the bushing 40. FIG. 30 shows an example of such an arrangement. In this case the bushing 40 may have undulations formed along its full length, unlike in the embodiment of FIG. 6a in which the bushing has a root end region 61 with a smooth cylindrical outer surface with no undulations.

It may be desirable to axially separate the functions of, on the one hand, transferring loads between a hub connection bolt and a bushing 40, and on the other hand, transferring loads between a bushing 40 and an insert body 108. Therefore, it may be desirable to axially offset the position of a thread 66, or other connection feature inside a bore 109 of a bushing 40, from the transition layer 102, which provides anchoring between the bushing and the insert body 108. To this end, as discussed the transition layer 102 may terminate axially inboard of a root end face of a bushing 40. At the same time, a thread 66 or other connection feature inside a bore 109 may be positioned at an end region of the bushing 40 axially offset from the transition layer 102. At the same time, in embodiments, the battens 148 may terminate at the end of the body region 59 where it meets the end region 61. In particular, the battens 148 in the body 108 of an insert blank 190 may terminate short of a root face end 232 of an insert or bushing 40. In this case, one-piece, flexible end caps 310 may be fitted over the end regions 61. The end caps may in particular have the required square or trapezoidal outer profile of the insert body 108. An example of such an end cap 310 is shown in FIG. 31. The illustrated end cap 310 may have four corner lobes 312 with the required deltoid cross-section, and a bore with a smooth cylindrical inner surface 311 which abuts the smooth cylindrical outer surface of the bushing end region 61. The end cap 310 may prevent the ingress of water or oil into the insert body 108.

Preferably, the end cap 310 may be formed from a low modulus plastic material. For example, the end cap 310 may be formed from a material with a modulus less than 1 GPa, which is much less than the modulus of the battens 148 (typically of the order of 40 GPa). The relatively low modulus of the end cap 310 ensures a simple stress field with the primary load path from the internal thread 66 into the battens 148 being via the body region 59 and the transition layer 102, and not via the end cap 310. The end cap 310 may optionally be glued in place.

FIG. 33 shows a blank 190 with a further alternative geometry. In the embodiment illustrated in FIG. 33, each triangular facet 202 a, b may run along only half the length of the transition portion 200 up to a vertical edge 205.

Although the invention has been described above with reference to one or more preferred embodiments, it will be appreciated that various changes or modifications may be made without departing from the scope of the invention as defined in the appended claims. 

1. An insert for a wind turbine blade root, the insert comprising: an insert body; a bushing with a threaded bore and an outer surface with circumferential grooves; and a transition layer comprising fibrous plies covering the bushing outer surface, and windings over said fibrous plies such that successive said plies alternate with said windings, wherein each fibrous ply is anchored into the grooves by an associated set of said windings, and said insert body surrounds said transition layer.
 2. The insert according to claim 1, wherein one or more of the sets of said windings have multiple windings per groove.
 3. The insert according to claim 2, wherein one or more of the sets of said windings have a number of windings per groove greater than a number of windings per groove of a set of said windings anchoring a lower fibrous layer.
 4. The insert according to claim 1, wherein each winding comprises a bundle of filaments, and the number of said filaments per groove applied over successive fibrous plies increases in a radial direction away from the bushing.
 5. The insert according to claim 1, wherein the circumferential grooves are circumferential annular grooves.
 6. The insert according to claim 5, wherein the circumferential annular grooves alternate with circumferential annular ridges, and the windings are formed by a filamentary material with connecting sections of the filamentary material which ride over the circumferential annular ridges between the circumferential annular grooves and connect together windings in adjacent circumferential annular grooves.
 7. The insert according to claim 1, wherein the threaded bore has an internal thread, wherein the bushing comprises an end region which contains the threaded bore and a body region which has the outer surface with the circumferential grooves, and wherein the end region is offset from the body region so that none of the grooves encircle the internal thread.
 8. The insert according to claim 1, wherein the grooves have a depth A and are separated by a pitch P, and the ratio A/P is less than one.
 9. The insert according to claim 1, wherein the outer surface of the bushing has a sectional profile across the grooves with a series of crests and troughs; and the crests and/or the troughs are rounded.
 10. The insert according to claim 1, wherein the insert body comprises two or more fibrous battens fitted around the transition layer, and each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section.
 11. An insert for a wind turbine blade root, the insert comprising a bushing embedded in an insert body, said bushing having a threaded bore, wherein said insert body comprises two or more fibrous battens fitted around the bushing, and each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section.
 12. The insert according to claim 11, further comprising a fibrous transition layer between said bushing and said insert body, in particular, between said bushing and said battens.
 13. The insert according to claim 10, wherein said two or more fibrous battens comprise four fibrous battens.
 14. The insert according to claim 10, wherein said two or more fibrous battens comprises two fibrous battens in the form of pultruded preforms, each pultruded preform having a pair of lobes, wherein each lobe has a deltoid cross-section.
 15. The insert according to claim 10, further comprising a fibrous outer shell around the fibrous battens.
 16. The insert according to claim 10, wherein each batten comprises a pultruded preform; or an assembly of fibrous rods; or rope.
 17. The insert according to claim 10, wherein the insert extends in a lengthwise direction, and the fibrous battens comprise fibres extending substantially in the lengthwise direction.
 18. A wind turbine blade comprising: a root and a tip, the wind turbine blade extending from the root to the tip; and a plurality of inserts according to claim 1 embedded in the root.
 19. A method of manufacturing an insert for a wind turbine blade root, the method comprising: providing a bushing, wherein the bushing has a threaded bore and an outer surface with circumferential grooves; wrapping a first fibrous ply around the bushing so that it overlies the grooves; winding filamentary material around the first fibrous ply to form a first set of windings which draw the fibrous ply into the grooves so that the first fibrous ply is anchored into the grooves by the first set of windings, the first set of windings and the first fibrous ply forming a transition layer around the bushing; positioning material around the transition layer to form an insert body; placing the bushing, the transition layer and the insert body in an infusion mould; injecting a matrix material into the infusion mould so that the matrix material infuses the transition layer; and curing the matrix material to form an insert body with an embedded bushing.
 20. The method according to claim 19 further comprising: wrapping a second fibrous ply around the bushing so that it overlies the grooves; and winding filamentary material around the second fibrous ply to form a second set of windings which draw the second fibrous ply into the grooves so that the second fibrous ply is anchored into the grooves by the second set of windings, wherein the first and second sets of windings and the first and second fibrous plies form the transition layer, and the first and second sets of windings alternate with the first and second fibrous plies.
 21. The method according to claim 19 wherein the first and/or second set of windings has multiple windings per groove.
 22. The method according to claim 19, comprising fitting two or more fibrous battens around the transition layer to form the insert body, wherein each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section.
 23. A method of manufacturing an insert for a wind turbine blade root, the method comprising: providing a bushing, wherein the bushing has a threaded bore; fitting two or more fibrous battens around the bushing, wherein each batten has a deltoid cross-section so that the battens give the insert a quadrilateral cross-section; placing the bushing and the battens in an infusion mould; injecting a matrix material into the infusion mould so that the matrix material infuses the insert; and curing the matrix material to form an insert body with an embedded bushing.
 24. The method according to claim 23, wherein the infusion mould comprises first and second mould parts which meet at a split line; and the split line coincides with a diagonal of the quadrilateral cross-section.
 25. The method according to claim 23 further comprising wrapping a fibrous transition layer around the bushing so that the fibrous battens are fitted around the transition layer, wherein the matrix material infuses the fibrous transition layer such that said transition layer forms an interface between said bushing and said insert body.
 26. The method according to claim 23, further comprising wrapping a fibrous outer shell around the fibrous battens, wherein the matrix material infuses the fibrous outer shell.
 27. The method according to claim 19, wherein the infusion mould comprises a mould cavity, and at least part of the mould cavity has a quadrilateral cross-section. 